processing information SIBUGLAS

D      EN

ground preparation for gluing

The ground must be dry and smooth, and free from loose material, dust, dirt, grease, wax and silicone. SIBU patterned sheets should never be mounted onto an uneven surface, as this results in a loss of visual quality.
In the case of convex and concave surfaces, the sheet edges must be fixed mechanically (except for MultiStyle).

Non-absorbent surfaces
In order to achieve maximum adhesion, always clean non-absorbent surfaces with alcohol  (ethanol, isopropyl alcohol).
Self-adhesive (SA) sheets are ideally suited to non-absorbent surfaces such as coated MDF/chipboard, glass, metal, plastic, etc. However, they are unsuitable for use on ceilings. Alternative processing options are available on request.

Absorbent surfaces
A solvent-free adhesive, which is suitable for both the underlying surface and the polystyrene material, must be employed on absorbent grounds, e.g. uncoated chipboard, MDF, plasterboard, or smoothed brickwork. Sibu recommendation: SIBUKLE.

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

General bonding information

Patterned sheets delivered in rolled form must be kept flat for a minimum of 24 hours. Weighing down improves evenness.
Ideal processing temperatures range from + 10 °C to + 30 °C. The design sheets must be acclimatised, i.e. be brought to room temperature prior to processing (avoidance of condensation on the gluing surface and a reduction in sheet expansion due to reduced temperature differences).
A temperature increase of 10 °C will cause our products to expand by approx. 0.7 mm over a length of 1 m.
As a rule, an approx. 2-3 mm expansion joint is to be left along the sheet edges!
In the case of high ambient temperatures, or major temperature fluctuations, the expansion gap should be increased, or a smaller sheet format selected.
Remove the paper backing from the reverse side of self-adhesive patterned sheets (SA) step-by-step. Do not touch the adhesive surface and press the sheet onto the ground as firmly as possible. Avoid the formation of bubbles (air inclusions) and use a medium-hard, rubber roller with a width of approx. 170 mm.
Full adhesion will be reached at room temperature after 24 hours.
Whenever possible, SIBU DESIGN products should be processed within 12 months (except for PVA pre-treated products).
They are not recommended for use near open fires or sources of intense heat.

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

processing SIBUKLE

Applications: SIBUKLE D 22 HV is ideally suited to the bonding of SIBU products onto absorbent, even surfaces such as wood, plywood, chipboard, plasterboard, or smooth brickwork. The underlying surface must be absorbent (MDF, chipboard, etc.).
WARNING! SIBUKLE D 22 HV is not unsuitable for non-absorbent grounds such as tiles, plastics, metals and glass, etc.
As a rule, an approx. 2 to 3 mm expansion joint is to be left along the sheet edges!
Processing: Apply only to the cleaned surface, which has been prepared for bonding, using a fine spatula (the spatula toothing for every product is provided in the OVERVIEW catalogue). With an ambient temperature of between 20 °C and 35 °C, the adhesive should then be left to air for 20 to 40 minutes. No drying time is required for PNL products, which are to be bonded in a wet adhesive bed. Fix mechanically if necessary, until the adhesive has hardened.
The higher the ambient temperature, the shorter is the airing time.
Finger test: following application with the spatula, the optimal airing time is reached as soon as the adhesive no longer sticks to the fingers!
Avoid the formation of bubbles (air inclusions) and use a medium-hard, rubber roller with a width of approx. 170 mm.
Storage: In the original airtight containers, the adhesive can be stored for up to 12 months from the delivery date. The goods should always be kept at above the freezing point.
If other solvent-free dispersion adhesives are employed, the respective processing instructions are to be followed. 

Please study the technical table in the overview in order to see if this accessory is suitable for your product.

cutting

SIBU Deco-Line sheets with less than 2 mm thickness can be easily cut with a wallpaper knife. Simply notch the surface and break about the edge. For all other product lines and for DECO-LINE sheets up to 3 mm thickness the cutting pressure has to be increased. After cutting and breaking our self adhesive (SA) design sheets as well as 3D PUNCH-LINE designs (NA + SA) the foil on the back side has to be cut separately. Always use well sharp knives. For mechanical cutting, we recommend the use of paper or veneer cutting machines.

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

punching/drilling

PUNCHING Band steel cutting is recommended for design sheets in thickness from 1 up to 1.5 mm.

DRILLING All SIBU design sheets can be drilled from the decor side.

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

sawing

SIBU guideline values:
Material thicknesses of up to 1 mm: HW 280x3.2 / 2.2x30 Z60 / 12.46-18.08 WZ
Thicker than 1 mm: HW 250x3.2 / 2.2x30 Z40 / 19.63 WZ/FA - HW 250x3.2 / 2.2x30 Z40 / 19.63 FZ/TR (speed 6000 rpm, progressive feed of up to 25 m/min).
For LEATHER-LINE: HW 255x2.8 / 2.0x30 Z80 / 10.01 FZ WZ (speed 6000 rpm, progressive feed of up to 10 m/min).
The best result with LEATHER-LINE is achieved with MDF underlay (4 mm) above and below, slow progressive feed and high speed.

*HW (hard metal material), WZ/FA (alternating teeth/bevelled edge), FZ (flat teeth), TR (trapezoidal teeth)

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

milling

For material with a thickness of up to 2 mm: employ a cutter with a 3 mm-diameter, a rotation speed of 12,000 to 24,000 rpm and a progressive feed of up to 12 m/min.
The patterned side on top: milling cutter with a left-hand twist, cutting right.
The patterned side below: milling cutter with a right-hand twist, cutting right. For material with a thickness of more than 2 mm, reduce the progressive feed and use a milling cutter with a larger diameter (6 mm).

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

laser-cutting

SIBU design sheets can be processed with standard lasers. The cutting speed is in line with the wattage of the laser.
To ascertain if the chosen product is suitable, please check the technical table in our OVERVIEW catalogue, or go to www.sibu.at.

Please study the technical table in the overview in order to see if this processing step is permissible for your product.

printing

Whether or not a SIBU product is recommended for printing can be ascertained from the technical table in our OVERVIEW catalogue, or at www.sibu.at. Owing to the many differing printing and colour systems, customers must carry out a printing test. The result will depend on the respective motif. We will be pleased to provide original samples for testing.

Please study the technical table in the overview in order to see if this processing step is permissible for your product.